General purpose polystyrene model: LV-T3N
Product Features: Good strength, high heat resistance, high transparency Application Overview: Extrusion foam, sheet, plate and other extrusion applications
Categories：
Material Chemistry
Email：sale06@alfachem.cn
Product introduction
| General purpose polystyrene model: LV-T3N | |||||
| Product description | |||||
| Specification level | Universal extrusion grade | Appearance color | Transparent granules | ||
| Product Features | Good strength, high heat resistance, high transparency | ||||
| Overview of uses | Extrusion foam, sheet, plate and other extrusion applications | ||||
| Product technical data | |||||
| Performance Items | Test conditions | Test Method | Typical values | Unit | |
| Basic Performance | Melt flow rate | 200℃/5kg | ASTM D1238 | 2.5-4.0 | g/10min |
| Density | 23/23℃ | ASTM D792 | 1.05 | g/cm3 | |
| Thermal performance | Vicat softening point | B50/oil | ISO306 | 97-100 | ℃ |
| Mechanical properties | Cantilever beam impact strength IZOD | 23℃ | ISO180 | 23-25 | J/m |
| Impact strength of simply supported beam | 23℃ | ISO 179 | 10 | KJ/m2 | |
| Tensile elongation at break EL% | 23℃ | ISO 527 | 2 | % | |
| Tensile yield strength TSY | 23℃ | ISO 527 | 42-45 | MPa | |
| Other Performance | Residual monomer | -- | GB/T16867-1997 | 〈500 | ppm |
| Product usage instructions | |||||
| Processing conditions | ●Normal processing before 80 ℃ baking material about 2-3 hours | ||||
| ●Recommended injection temperature is 190-220℃ | |||||
| ●Do not leave the hot melt resin in the extrusion barrel for a long time during the extrusion process | |||||
Note: Typical performance is not a product specification
Key words:
Related Products
Related Products
Inquiry
Phone/WhatsApp:
Email:
Through its excellent service and product qualities, VT Chemical has cooperated with many famous customers all over the world, eg. TCI, Covestro, etc.
HUATAO GROUP
Leave Message
SAF Coolest v1.3.1.2 设置面板 MFBSX-AJYI-DZAAE-ZAQ
违禁词： 第一，最，一流，领先，独一无二，王者，龙头，领导者，极致，
无数据提示
Sorry, the current column is being updated, please look forward to it!
You can view other columns